Phenolic compounds in the soils collected from plow layers of greenhouse and field cultures were surveyed quantitatively by gas chromatography. The results are as follows : 1) p-Coumaric, ferulic, salicylic, p-hydroxybenzoic, vanillic, syringic, and protocatechuic acids were detected in all upland soils, as in the case of paddy and forest soils reported previously. Among these phenolics, p-coumaric acid was present in the largest quantity in most of the upland soils up to 29.0 ppm. 2) The total amounts of individual phenolic acids in the upland soils ranged from 9.5 to 62.0 ppm (average 26.0 ppm). Also, the amounts were less than 0.18% (average 0.10%) of the total soil organic matter. The average values in the upland soils were higher than those in the paddy soils, but were lower than those in the forest soils. 3) In upland soils, the concentrations of p-hydroxybenzoic, vanillic, syringic, p-coumaric, and ferulic acids, which have no chelating ability, were considerably related to the carbon content of soil, but the concentrations of protocatechuic and salicylic acids, which are chelating agents, were not related to that of soil. These relationships agreed with those found in paddy and forest soils.

Decomposition of organic nitrogenous materials in soil was affected by C/N ratio.Immobilization of nitrogen mineralized from nitrogenous material added to the soil was influenced by the degradability of carbonaceous and nitrogenous materials.The turnover of nitrogen which had been freshly immobilized in the presence of glucose in the soil was faster than that immobilized with cellulose or lignin. The effect of soil-drying on the mineralization of organic nitrogen immobilized through the decomposition of carbonaceous and nitrogenous materials in the soil depended significantly on the availability of carbonaceous materials as a microbial energy source.However, the drying effect was not always proportional to the amount of organic nitrogen accumulated in the soil.

電子サイクロトロン共鳴マイクロ波プラズマを利用したスパッタ成膜装置(ECRスパッタ装置)において、独自のパラメータであるマイクロ波電力に着目し、これを活用してCo-Cr-Ta/Ti垂直磁気ディスクの高性能化を試みた。プラズマ生成室に投入するマイクロ波電力を増加させると、生成されるプラズマ密度が増加し、成膜速度を高まること、成膜中に基板を照射するArイオンの量が増加することが明らかになった。Co-Cr-Ta膜の作製において、マイクロ波パワーを成膜初期には高パワーとし、途中からは低パワーに変更するという制御を行うことによって、グレインが微細で、磁気特性および記録特性に優れた垂直磁気ディスクをパワー一定とした従来よりも高速に作製できることを見出した。

誘導結合型プラズマ(ICP)を利用したマグネトロンスパッタ装置を試作し、Co-Cr垂直磁気異方性膜の作製を行った。誘導結合型プラズマ支援マグネトロンスパッタ装置では、高周波によるプラズマ生成と、ターゲットに印可した直流によるスパッタ成膜とが機能分離できているために、通常のマグネトロンスパッタ法ではプラズマの維持が不可能な低いターゲット電圧領域においてもCo-Cr薄膜の作成が可能なことが明らかになった。ICPを用いることで、通常のマグネトロンスパッタ法のみの場合よりも、高い成膜速度が実現できた。ICP電力を増すと、作製したCo-Cr膜の垂直磁気異方性は減少する傾向がみられた。大きな垂直磁気異方性をもつCo-Cr膜を高速に作製するには、ICPを用いることに加えて、正の基板バイアス電圧の印可を併用することが効果的であるとの見通しを得た。

ECRスパッタ法によりCo-Cr膜を作成したとき、その磁気特性と結晶学的特性は成膜中の基板を照射するイオン加速電圧に強く依存することか明らかとなった。このイオン加速電圧はArガス圧とターゲット-基板間距離により制御することができ、イオン加速電圧を20V以下に適正化した結果、50nmの厚さのCo-Cr膜で、優れた結晶配向性(5゜以下のΔθ_<50>)、高い垂直異方性磁界(4kOe以上のH_k)、高い垂直方向力(1400Oe以上のH_<c⊥>)が得ることができた。