Experimental Relationships between the Fracture Behaviour and the Specimen Thickness in Fe-Ni-Co-C Martensitic Steels

Memoirs of the Faculty of Engineering, Yamaguchi University Volume 33 Issue 2 Page 219-227
published_at 1983
KJ00000156461.pdf
[fulltext] 1.11 MB
Title
Fe-Ni-Co-C マルテンサイト鋼の破壊挙動と試片厚さについて
Experimental Relationships between the Fracture Behaviour and the Specimen Thickness in Fe-Ni-Co-C Martensitic Steels
Creators Takimoto Akio
Creators Shoda Shunji
Creators Kajiwara Hatsutaro
Creators Yuge Tetsuya
Source Identifiers
Thin film specimens of both about 5μm and 20μm thickness and the ASTM standard sheet specimens of 1.6mm thickness were prepared using Fe-Ni-Co-C martensitic steels and were fractured in tension at room temperatue and at -196℃. Results of thin film specimens were compared with those of the ASTM standard specimens which showed very brittle behaviour. Fractography was investigated under both an optical microscope and S. E. M., and even cleavage facets were observed in the 5μm thick specimens. The observed behaviour supports mechanical results pretty well. Discussion is made on the view points of plane stress and plane strain conditions and of machine stiffness. The technique employed here and the results obtained are also examined to give a good information on studying mechanical properties of amorphous metal films.
Subjects
機械工学 ( Other)
Languages jpn
Resource Type departmental bulletin paper
Publishers 山口大学工学部
Date Issued 1983
File Version Version of Record
Access Rights open access
Relations
[ISSN]0372-7661
[NCID]AN00244228
Schools 工学部