Fabrication and superconducting properties of Nb_3Al prepared from Nb_2Al and Nb powders

Memoirs of the Faculty of Engineering, Yamaguchi University Volume 46 Issue 1 Page 103-109
published_at 1995-10
KJ00000157032.pdf
[fulltext] 551 KB
Title
Nb_2AlとNbとの反応によるNb_3Alの製作と超伝導特性
Fabrication and superconducting properties of Nb_3Al prepared from Nb_2Al and Nb powders
Creators Harada Naoyuki
Creators Fukuda Yuji
Creators Ichikohara Hideki
Creators Osaki Katashi
Creators Tada Naofumi
Source Identifiers
Bulk and tape specimens of Nb_3Al have been fabricated by the powder metallurgy method between Nb_2Al and Nb. The microstructure and superconducting properties on the starting materials and the temperature of a heat treatment have been studied. X-ray diffraction analysis was carried out in order to identify the phases formed by the heat treatment. The A15 single phase, Nb_3Al, were formed at 1100℃ for the bulk specimen prepared from the Nb_2Al/Nb mixed powders. The temperature of a heat treatment formed the A15 single phase prepared from the Nb_2Al/Nb was down 100-200℃ in comparison to that prepared from the Nb/Al mixed powders. The highest critical temperature, Tc, obtained in the bulk specimens prepared from the Nb_2Al/Nb mixed powders is 16.0 K.
Languages jpn
Resource Type departmental bulletin paper
Publishers 山口大学工学部
Date Issued 1995-10
File Version Version of Record
Access Rights open access
Relations
[ISSN]0372-7661
[NCID]AN00244228
Schools 工学部