タイトル準安定オーステナイト鋼の加工変態と低サイクル疲労について
タイトルヨミジュン アンテイ オーステナイト コウ ノ カコウ ヘンタイ ト テイサイクル ヒロウ ニツイテ
タイトル別表記Strain Induced Martensitic Transformation and Low Cycle Fatigue in Metastable Austenitic Steels
作成者瀧本, 昭夫
恒松, 裕之
稲富, 俊隆
冨尾, 秀博
片倉, 和人
出口, 政美
作成者ヨミタキモト, アキオ
ツネマツ, ヒロユキ
イナトミ, トシタカ
トミオ, ヒデヒロ
カタクラ, カズオ
デグチ, マサミ
作成者別表記Takimoto, Akio
Tsunematsu, Hiroyuki
Inatomi, Toshitaka
Tomio, Hidehiro
Katakura, Kazuto
Deguchi, Masami
作成者所属山口大学工学部
内容記述(抄録等)The effect of strain induced martensite on the fatigue life was investigated in the air and brine by using metastable austenitic steels. A center hole, double edge key-hole or groove notches were introduced in tensile and fatigue specimens as elastic and plastic strain concentrators. Smooth specimens tested in tension exhibit the transformation product more in brine than in the air both in SUS 301 and 302. The induced martensite distribution around a center hole in tension shows a butterflywing type extent in the alloy D. In the air and brine a fatigue crack propagates in three stages both in SUS 301 and 302. The fatigue life in brine is always shorter than that in the air. The volume of induced martensite in brine is usually more than that in the air and it is confirmed that the transformation strats at the earlier cycle in brine than in the air in SUS 301. The crack growth rate per unit cycle in the second stage increases with the designed stress concentration factor on the key-hole and groove notch specimens and the complete reversed relationship is observed on the center hole specimen in which the stress gradient is seemed to be another important factor. The fringes around freshly propagated fatigue cracks, corroded by brine are often observed both in SUS 301 and 302.
本文言語jpn
主題機械工学
資料タイプtext
ファイル形式application/pdf
出版者山口大学工学部
出版者ヨミヤマグチ ダイガク コウガクブ
NII資料タイプ紀要論文
ISSN0372-7661
NCIDAN00244228
学内刊行物(紀要等)山口大学工学部研究報告
掲載誌名山口大学工学部研究報告
掲載誌名別表記Memoirs of the Faculty of Engineering, Yamaguchi University
32
1
開始ページ19
終了ページ21
発行日1981