タイトルB_2O_3-Fe_2O_3-RO (R=Ba, Sr, Ca, Zn) 系ガラスの磁気的性質
タイトルヨミB_2O_3-Fe_2O_3-RO R=Ba, Sr, Ca, Zn ケイ ガラス ノ ジキテキ セイシツ
タイトル別表記The Magnetic Susceptibities of B_2O_3-Fe_2O_3-RO (R : Ba, Sr, Ca, Zn) System Glasses
作成者矢田部, 俊一
中村, 秀樹
廣末, 孝行
平野, 泰隆
横道, 正克
作成者ヨミヤタベ, シュンイチ
ナカムラ, ヒデキ
ヒロスエ, タカユキ
ヒラノ, ヤスタカ
ヨコミチ, マサカツ
作成者別表記Yatabe, Shunichi
Nakamura, Hideki
Hirosue, Takayuki
Hirano, Yasutaka
Yokomichi, Masakatsu
作成者所属山口大学工学部
内容記述(抄録等)The magnetic properties of B_2O_3-Fe_2O_3-RO (R : Ba, Sr, Ca, Zn) system of glasses were studied in this paper. The glasses in this system were melted in electric furnace, about 1300℃, five hours. The melted glasses were powdered into particles of 80 meshes by agate mortar. The magnetic susceptibilities of the glasses were meaured by Gouy method. The results are as follows. 1) The magnetic susceptibilities are about 10-30×(10)^6(cm)^3g^<-1>, and are approximately equal to the susceptibility of Fe_2O_3 : 20.6×(10)^6(cm)^3g^<-1> (18℃) 2) The susceptibities are proportional to the contents of Fe_2O_3 mol in glasses and don't depend on the contents and species of other components in glasses.
本文言語jpn
主題プロセス工学・化学工学
資料タイプtext
ファイル形式application/pdf
出版者山口大学工学部
出版者ヨミヤマグチ ダイガク コウガクブ
NII資料タイプ紀要論文
ISSN0372-7661
NCIDAN00244228
学内刊行物(紀要等)山口大学工学部研究報告
掲載誌名山口大学工学部研究報告
掲載誌名別表記Memoirs of the Faculty of Engineering, Yamaguchi University
25
1
開始ページ25
終了ページ29
発行日1974
著者版/出版社版出版社版
備考本文データは国立情報学研究所において電子化したものである
リポジトリIDKJ00000156058
地域区分山口大学
URIhttp://www.lib.yamaguchi-u.ac.jp/yunoca/handle/KJ00000156058